High-strength plywood formwork using MR, WBP waterproof glue, the bottom of the film adopts high density imported red-brown bright color film and domestic high quality black film, light red-brown film, the product is impact-resistant, wear-resistant, easy to peel off, and the surface is smooth and flat , the physical properties are stable. The products have a variety of specifications for construction engineering general-purpose and special-purpose. types of plywood for formwork are widely used in large and medium-sized construction sites such as bridges, power plants, buildings, and high-rise buildings!
Main customer groups:
Foreign (especially European and American buyers), domestic distributors, domestic construction engineering companies.
Product specifications:
formwork plywood sizes (mm) | formwork plywood thickness |
1830*915 1220*2440 | 8 |
9 | |
10 | |
11 | |
18 |
Wood plywood performance parameters:
Parameter | Unit | Standard rating | Measured value |
Bonding strength | Mpa/m m² | ≥0.7 | 1.72 |
Moisture content | % | 6-14 | 9 |
Static bending strength | Mpa/m m² | ≥24 | 36 |
Elastic Modulus | Mpa/m m² | ≥5000 | 5017 |
Surface wear-resistant | g/100r | ≤0.08 | 0.04 |
Quality | Kg/sheet | 15 |
Plywood for formwork quality standards:
NO. | Item | Product Standards |
1 | Edge defec | None |
2 | Glue, fracture, delamination | None |
3 | Length tolerance | ±3mm |
4 | Thickness tolerance | 12±3mm/15±3mm /18±3mm |
5 | Diagonal tolerance | ±3mm |
6 | Warpage | No more than 1% |
7 | Surface depression, indentation, bulge | None (individual slight indentation is allowed) |
8 | Surface repai | None |
9 | Surface scratches, communication, scorching, burrs | None (individual slight indentation is allowed) |
10 | Laminated paper is opened, damaged, missing edges | None |
11 | Discoloration | None |
12 | Splicing cracks on the table boar | None |
13 | Table laminate | None |
14 | Patch | None |
15 | Moisture content | 6-10% |
16 | Bonding strength | ≥0.8 |
High grade laminated plywood formwork for concrete has the following characteristics:
1. The surface of the 18mm film faced formwork plywood is processed by precision machinery with imported film-coated paper, which has high flatness, smooth and easy to demould, and the concrete surface is flat and smooth. Plastering can be cancelled, shortening the construction period, and it is light in weight, easy to saw and nail. It has good construction performance, and can be made of various special-shaped boards with high construction efficiency.
2. The concrete formwork plywood has a wide breadth, fewer seams. Compared with the steel template, the speed of supporting and dismantling the mold is faster.
3. The laminated building plywood formwork is made of high temperature and high pressure and pressed, with good toughness, and the static bending strength is more than twice the strength of wood.
4. When the high-grade concrete formwork plywood is removed, the concrete will not be impacted and vibrated;
5. The plywood formwork has strong water resistance. It is made of phenolic resin by hot pressing during production. The glue will not be opened after boiling for 4 hours, and the concrete will not deform when exposed to water during the curing process.
6. The thermal conductivity of the plywood formwork for concrete is much lower than that of the steel mold, which is beneficial for winter construction.
7. The use turnover frequency of concrete form plywood is high, which can reach more than 10 times.
8. ply shuttering concrete are suitable for horizontal templates, shear walls, vertical wall panels, viaducts, overpasses, ridges, tunnels and beam and column templates of high-rise buildings.
In order to ensure the normal use of film faced shuttering plywood, the following points should be noted:
1. For the positioning frame and metal connecting rods permanently buried in the concrete, the distance between them shall not be less than 5cm, and the holes formed by the connecting rods shall be blocked.
2. The joints of the film faced shuttering plywood must be installed tightly to prevent the loss of cement slurry. At the construction joints, the formwork must firmly clamp the poured concrete to avoid unevenness of the exposed surface of the joint.